我国炼焦煤资源供需矛盾突出,配入无烟煤炼焦是降低生产成本并扩大煤种资源利用的有效途径,无烟煤粒度对焦炭质量的影响研究可用于指导无烟煤在配煤炼焦中的技术应用。以典型1/3焦煤和不同粒度的无烟煤为研究对象,结合煤质特性分析并通过40kg小焦炉开展炼焦实验。由研究发现,配入无烟煤可使焦炭的灰分降低、固定碳含量升高以及发热量提升。焦炭块度随无烟煤粒度减小而增大,表面平整且气孔均匀分布,当粒度大于3mm时,焦炭易碎且无烟煤颗粒明显可见。焦炭强度随无烟煤粒度增加而降低,当无烟煤粒度小于0.5mm时,焦炭CSR为70.1%,M40为88.4%。当无烟煤配入粒度小于0.5mm时,焦炭平均粒度为52.0mm,其粒度分布集中于40~60mm,该区段粒度占比为56.82%。无烟煤配入粒度小于3.0mm时均可满足高炉运行要求。实验证明配入粒度小于0.5mm的无烟煤时,焦炭质量得到显著提升,从而可扩大炼焦煤种资源并实现降本增效。

The contradiction between the supply and demand of coking coal resources in China is prominent. Incorpo⁃rating anthracite into the coking process proves to be an effective approach for reducing production costs and expandingthe utilization of coal resources. The study on the influence of anthracite particle size on coke quality can provideguidance for the technical application of anthracite in coking coal blending. By focusing on the typical 1 / 3 coking coaland anthracite with varying particle sizes, combined with analysis of coal quality characteristics, coking experimentswere conducted using a 40 kg small coke oven. It was observed that adding anthracite can decrease the ash content,increase fixed carbon content, and enhance calorific value in coke production. Additionally, as the particle size ofanthracite decreases, there is an increase in coke lumpiness with a flat surface and evenly distributed pores. Whenthe particle size of anthracite exceeds 3 mm, coke becomes brittle and visible particles of anthracite are evident. Fur⁃thermore, increasing the particle size of anthracite leads to decreased coke strength, when anthracite particles issmaller than 0. 5 mm in size, CSR of coke reaches 70. 1% while M40 index achieves 88. 4%. Moreover, when an⁃thracite coal is added with a particle size less than 0. 5 mm, the average particle size of coke is 52. 0 mm, its particlesize distribution is concentrated in 40-60 mm, the granularity of this section accounts for 56. 82%. When the size ofanthracite is less than 3. 0 mm, it can meet the operation requirements of blast furnace. The experiments demonstratethat incorporating fine⁃sized (<0. 5 mm) anthracites can significantly improve coke quality, this can expand cokingcoal resources and achieve cost reduction and efficiency improvement.

煤科院科技发展基金资助项目(2021CX-Ι-01)

朱汝斌, 曹强. 无烟煤粒度对焦炭质量的影响研究 [J]. 煤质技术, 2024, 39 (1): 61-67.

ZHU Rubin, CAO Qiang. Research on the influence of anthracite particle size on quality of coke [J]. Coal QualityTechnology, 2024, 39 (1): 61-67.